Sunscreens exposed: stripping away the gloss
Gregory Crocetti
With the help of the students from Trinity College, Colac, Friends of the Earth has completed a Citizen Science Experiment investigating the effect that a number of popular Australian sunscreens have on the coating of Colorbond steel and on varnished timber. The results from the Colorbond steel were inconclusive. However, several popular sunscreens containing nanoparticles − including Nivea Kids Swim and Play − were found to cause serious damage to the wood varnish. These results are consistent with Barker and Branch's 2008 study and raise serious concerns about the continued use of nanoparticles of anatase titanium dioxide in sunscreen.
In 2008, industrial chemists Phil Barker and Amos Branch from Blue Scope Steel confirmed what many had suspected – that the new use of nanoparticles in sunscreens posed novel and uncertain risks. Of particular concern to these researchers was the use of sunscreens containing nanoparticles of anatase titanium dioxide by roofing installers, which came into contact with and caused damage to Colorbond panels as they were being installed. The scientists observed that the nanoparticles in the sunscreen were reacting with the sun to create free radicals, which were causing the roof coatings to break down up to 100 times faster than normal.
The project with Trinity College repeated key aspects of the Blue Scope Steel research – particularly the exterior exposure testing. This measured the extent of gloss reduction in pre-painted steel products that were exposed to different sunscreen formulations over a 12-week period. The experiment also investigated the extent of gloss reduction in wood panels coated with a popular weatherproof timber varnish.
Two matching sets of 17 steel and timber panels were prepared – one for each of the different sunscreens tested and one control. Sixteen different sunscreens were tested containing either chemical or mineral-based active ingredients. These were applied to the bottom half of each panel.
The two matching sets of panels were secured onto the roof of Colac Trinity College and a residential house in Melbourne and exposed from mid-November 2012 to mid-February 2013.
Following the 12-week exposure, sunscreen was removed by rubbing the panel surface with soft paper towels soaked with a warm detergent solution for approximately one minute, and then rinsed with water and air dried. Initial gloss measurements were made by students at Colac Trinity College, followed by measurements using a 60˚ gloss meter (Byk-Gardner) by Dr. Gregory Crocetti. Five gloss meter readings were taken from each half of each panel and used to calculate means and standard errors.
Visual observations by students largely agreed with the gloss meter readings. Results from the Colorbond exposure experiment did not offer any conclusive findings. However, clear trends emerged from both replicates of the timber panel exposure experiments. It was found that almost all sunscreens were able to remove some of the gloss from the polyurethane timber varnish, with an average gloss reduction of 41.5 % across the 16 tested sunscreens.
Nivea Kids Swim and Play sunscreen caused the largest amount of gloss reduction across all timber panels with an average gloss reduction measurement of 82.9 % ± 5.7 averaged from both Melbourne and Colac panels. In stark contrast, the average gloss reduction from both control panels was recorded at 0.3% ± 7.8, confirming that the gloss varnish did not naturally degrade during the 12 weeks of exterior exposure.
The results of this study are consistent with the 2008 Barker and Branch study, which found that sunscreens containing nanoparticles of anatase titanium dioxide had the greatest potential to create dangerous free radicals.
Take action: turn up the heat on the government
Please contact the Parliamentary Secretary for Health, Catherine King and demand an immediate ban on the use of anatase TiO2 in sunscreens and the proper safety testing and labelling of all nano-ingredients in sunscreen:
The Hon Catherine King MP
PO Box 6022
House of Representatives
Parliament House
Canberra ACT 2600
Tel: (02) 6277 4230 Email: Catherine.King.MP@aph.gov.au
Or contact her via our website: http://nano.archive.foe.org.au